● Maximum sliding speed, U:5.0m/s
● Maximum Operating Temperature Tmax:280 °C
● Minimum Operating Temperature Tmin:-200 °C
● Maximum pU factor:1.0N/mm² x m/s

● Thermal Conductivity40 W/mK
● Maximum Operating Temperature Tmax280 °C
● Minimum Operating Temperature Tmin-200 °C
● Compressive Yield Strength350 N/mm2

● Thermal Conductivity40 W/mK
● Maximum Operating Temperature Tmax280 °C
● Minimum Operating Temperature Tmin-200 °C
● Compressive Yield Strength350 N/mm2

● Hardness HB90-HB125
● Yield point250 N/mm2
● Tensile strength450 N/mm2
● Maximum Dynamic Load40 N/mm2

● Hardness HB90-HB125
● Yield point250 N/mm2
● Tensile strength450 N/mm2
● Maximum Dynamic Load40 N/mm2

● Hardness125-150 HB
● Yield point300 N/mm2
● Tensile strenght450 N/mm2
● Maximum Dynamic Load40 N/mm2

● Maximum Operating Temperature Tmax-greased150 °C
● Maximum Operating Temperature Tmax-oil lubricated250 °C
● Minimum Operating Temperature Tmin-40 °C
● Maximum Static Load Psta,max300 N/mm2

● Maximum Operating Temperature Tmax-greased150 °C
● Maximum Operating Temperature Tmax-oil lubricated250 °C
● Minimum Operating Temperature Tmin-40 °C
● Maximum Static Load Psta,max300 N/mm2

●
●
●
●

●
●
●
●

● Max. dynamic load100N/mm2
● Max. Temperature300 [ °C ]
● Base HardnessHB210-270
● Friction coefficient<0.16

● Basic MaterialsCu663,SAE841,SINT A50
● Other MaterialsSINT B50,SINT B51, SINT C51
● Oil rate≥18%
● Hardness20HB-50HB

● Basic MaterialsIron,SAE863,ASTM B439-70
● Other MaterialsSINT - B00,SINT - B11
● Oil rate≥18%
● Hardness40HB~70HB

● Basic MaterialsCu663,SAE841,Iron,SAE863
● Oil rate≥18%
● Hardness20HB-50HB
● ApplicationFan motor,electrical motor

● Max Load Capacity2 30N/mm2
● Shrink Fit0.01mm~0.02mm
● Max Sliding Speed6m/s
● Coef Friction0.01~0.08

● Max Load Capacity230N/mm2
● Shrink Fit0.01mm~0.02mm
● Max Sliding Speed6m/s
● Coef Friction0.01~0.08

● Max Load Capacity2 30N/mm2
● Shrink Fit0.01mm~0.02mm
● Max Sliding Speed6m/s
● Coef Friction0.01~0.08

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●

●
●
●
●